| Young's modulus | 150000 | MPa |
| Tensile strength | 0 | MPa |
| Compressive strength | 2000 | MPa |
| Bending strength | 250 | MPa |
| Hardness | 1200 | Vickers |
| Yield strength | 0 | MPa |
| Thermal expansion | 10 | E-6/K |
| Thermal conductivity | 2.5 | W/m*K |
| Specific heat | 500 | J/kg*K |
| Minimum service temperature | 0 | °C |
| Maximum service temperature | 2000 | °C |
| Density | 5800 | kg/m3 |
| Resistivity | 10-15/3.0 | Ohm*mm2/m |
| Friction coefficient | 0 | |
| Main constituent | 90 | |
| Average grain size | 2.5 | μm |
| Fracture toughness | 6 | MN/m3/2 |