Young's modulus | 1050 | MPa |
Tensile strength | 27.5 | MPa |
Elongation | 650 | % |
Bending strength | 24.5 | MPa |
Hardness | 66 | Shore |
Impact strength | 0.635 | J/cm |
Yield strength | 26 | MPa |
Thermal expansion | 180 | E-6/K |
Thermal conductivity | 0.22 | W/m*K |
Vicat | 90 | °C |
Melting temperature | 162.5 | °C |
Glass temperature | -10 | °C |
Minimum service temperature | -10 | °C |
Maximum service temperature | 110 | °C |
Density | 904.5 | kg/m3 |
Resistivity | 5E+21 | Ohm*mm2/m |
Breakdown potential | 72.5 | kV/mm |
Dielectric loss factor | 0.0004 | |
Friction coefficient | 0.4 | |
Refraction index | 1.5 | |
Shrinkage | 1.4 | % |
Water absorption | 0.01 | % |