| Young's modulus | 1935 | MPa |
| Shear modulus | 400 | MPa |
| Tensile strength | 45 | MPa |
| Elongation | 210 | % |
| Bending strength | 77.5 | MPa |
| Hardness | 106 | Rockwell |
| Impact strength | 1.25 | J/cm |
| Yield strength | 0 | MPa |
| Thermal expansion | 90 | E-6/K |
| Thermal conductivity | 0.231 | W/m*K |
| Specific heat | 1185 | J/kg*K |
| Vicat | 155 | °C |
| Melting temperature | 190 | °C |
| Minimum service temperature | -70 | °C |
| Maximum service temperature | 80 | °C |
| Density | 1015 | kg/m3 |
| Resistivity | 1E+17 | Ohm*mm2/m |
| Breakdown potential | 40 | kV/mm |
| Dielectric loss factor | 0.035 | |
| Friction coefficient | 0.35 | |
| Shrinkage | 1.2 | % |
| Water absorption | 1.525 | % |