| Young's modulus | 3650 | MPa |
| Shear modulus | 1380 | MPa |
| Tensile strength | 75 | MPa |
| Elongation | 3.5 | % |
| Fatigue | 27 | MPa |
| Bending strength | 125 | MPa |
| Hardness | 80 | Rockwell |
| Impact strength | 0.25 | J/cm |
| Yield strength | 0 | MPa |
| Thermal expansion | 70 | E-6/K |
| Thermal conductivity | 0.15 | W/m*K |
| Specific heat | 1180 | J/kg*K |
| Glass temperature | 101 | °C |
| Minimum service temperature | -20 | °C |
| Maximum service temperature | 90 | °C |
| Density | 1070 | kg/m3 |
| Resistivity | 1E+20 | Ohm*mm2/m |
| Breakdown potential | 160 | kV/mm |
| Dielectric loss factor | 4.5E-5 | |
| Friction coefficient | 0.52 | |
| Refraction index | 1.567 | |
| Shrinkage | 0.55 | % |
| Water absorption | 0.4 | % |