| Young's modulus | 575 | MPa |
| Shear modulus | 230 | MPa |
| Tensile strength | 30.5 | MPa |
| Elongation | 450 | % |
| Compressive strength | 23.5 | MPa |
| Bending strength | 5.5 | MPa |
| Hardness | 54 | Rockwell |
| Impact strength | 1.6 | J/cm |
| Yield strength | 0 | MPa |
| Thermal expansion | 80 | E-6/K |
| Thermal conductivity | 0.24 | W/m*K |
| Specific heat | 1000 | J/kg*K |
| Melting temperature | 327 | °C |
| Glass temperature | 127 | °C |
| Minimum service temperature | -200 | °C |
| Maximum service temperature | 260 | °C |
| Density | 2175 | kg/m3 |
| Resistivity | 1E+22 | Ohm*mm2/m |
| Breakdown potential | 65 | kV/mm |
| Dielectric loss factor | 0.00035 | |
| Friction coefficient | 0.075 | |
| Refraction index | 1.35 | |
| Shrinkage | 4.75 | % |
| Water absorption | 0 | % |