PA66

Polyamide 6.6

Young's modulus 1850 MPa
Shear modulus 1150 MPa
Tensile strength 82.5 MPa
Elongation 156 %
Compressive strength 66 MPa
Fatigue 22 MPa
Bending strength 120 MPa
Hardness 115 Rockwell
Impact strength 0.99 J/cm
Yield strength 0 MPa
Thermal expansion 85 E-6/K
Thermal conductivity 0.2575 W/m*K
Specific heat 1670 J/kg*K
Vicat 200 °C
Melting temperature 257.5 °C
Glass temperature 78 °C
Minimum service temperature -60 °C
Maximum service temperature 160 °C
Density 1140 kg/m3
Resistivity 1E+19 Ohm*mm2/m
Breakdown potential 16.85 kV/mm
Dielectric loss factor 0.027
Friction coefficient 0.335
Refraction index 1.53
Shrinkage 1.15 %
Water absorption 3.25 %