| Young's modulus | 2150 | MPa |
| Shear modulus | 890 | MPa |
| Tensile strength | 37 | MPa |
| Elongation | 42.5 | % |
| Compressive strength | 44.75 | MPa |
| Fatigue | 12 | MPa |
| Bending strength | 68.5 | MPa |
| Hardness | 75 | Rockwell |
| Impact strength | 2.635 | J/cm |
| Yield strength | 0 | MPa |
| Thermal expansion | 52 | E-6/K |
| Thermal conductivity | 0.15 | W/m*K |
| Specific heat | 1402.5 | J/kg*K |
| Vicat | 93.5 | °C |
| Minimum service temperature | -40 | °C |
| Maximum service temperature | 75 | °C |
| Density | 1050 | kg/m3 |
| Resistivity | 1E+17 | Ohm*mm2/m |
| Breakdown potential | 70 | kV/mm |
| Dielectric loss factor | 0.0012 | |
| Friction coefficient | 0 | |
| Shrinkage | 0.55 | % |
| Water absorption | 0.325 | % |