| Young's modulus | 1600 | MPa |
| Tensile strength | 40 | MPa |
| Elongation | 2.5 | % |
| Compressive strength | 165 | MPa |
| Fatigue | 7.5 | MPa |
| Bending strength | 45 | MPa |
| Hardness | 90.5 | Janka |
| Yield strength | 0 | MPa |
| Thermal expansion | 115 | E-6/K |
| Thermal conductivity | 0.21 | W/m*K |
| Specific heat | 1380 | J/kg*K |
| Melting temperature | 210 | °C |
| Glass temperature | 70 | °C |
| Minimum service temperature | -40 | °C |
| Maximum service temperature | 75 | °C |
| Density | 1300 | kg/m3 |
| Resistivity | 1E+17 | Ohm*mm2/m |
| Breakdown potential | 37 | kV/mm |
| Dielectric loss factor | 0.0095 | |
| Friction coefficient | 0 | |
| Refraction index | 1.49 | |
| Shrinkage | 0.55 | % |