| Young's modulus | 25000 | MPa |
| Tensile strength | 180 | MPa |
| Elongation | 4.6 | % |
| Compressive strength | 80 | MPa |
| Bending strength | 220 | MPa |
| Impact strength | 2.915 | J/cm |
| Yield strength | 0 | MPa |
| Thermal expansion | 55 | E-6/K |
| Melting temperature | 345 | °C |
| Minimum service temperature | -100 | °C |
| Maximum service temperature | 260 | °C |
| Density | 1235 | kg/m3 |
| Resistivity | 1E+19 | Ohm*mm2/m |
| Breakdown potential | 37 | kV/mm |
| Dielectric loss factor | 0.0035 | |
| Friction coefficient | 0.4 | |
| Shrinkage | 0.6 | % |
| Water absorption | 0.06 | % |