| Young's modulus | 1050 | MPa |
| Tensile strength | 27.5 | MPa |
| Elongation | 650 | % |
| Bending strength | 24.5 | MPa |
| Hardness | 66 | Shore |
| Impact strength | 0.635 | J/cm |
| Yield strength | 26 | MPa |
| Thermal expansion | 180 | E-6/K |
| Thermal conductivity | 0.22 | W/m*K |
| Vicat | 90 | °C |
| Melting temperature | 162.5 | °C |
| Glass temperature | -10 | °C |
| Minimum service temperature | -10 | °C |
| Maximum service temperature | 110 | °C |
| Density | 904.5 | kg/m3 |
| Resistivity | 5E+21 | Ohm*mm2/m |
| Breakdown potential | 72.5 | kV/mm |
| Dielectric loss factor | 0.0004 | |
| Friction coefficient | 0.4 | |
| Refraction index | 1.5 | |
| Shrinkage | 1.4 | % |
| Water absorption | 0.01 | % |