| Young's modulus | 2400 | MPa |
| Tensile strength | 60 | MPa |
| Elongation | 25 | % |
| Compressive strength | 111.5 | MPa |
| Fatigue | 15.5 | MPa |
| Bending strength | 95 | MPa |
| Hardness | 117 | Rockwell |
| Impact strength | 0.955 | J/cm |
| Yield strength | 0 | MPa |
| Thermal expansion | 61 | E-6/K |
| Thermal conductivity | 0.193 | W/m*K |
| Specific heat | 1295 | J/kg*K |
| Vicat | 130 | °C |
| Melting temperature | 272.5 | °C |
| Minimum service temperature | -100 | °C |
| Maximum service temperature | 120 | °C |
| Density | 990 | kg/m3 |
| Resistivity | 1E+21 | Ohm*mm2/m |
| Breakdown potential | 45 | kV/mm |
| Dielectric loss factor | 0.00054 | |
| Friction coefficient | 0.225 | |
| Shrinkage | 0.6 | % |
| Water absorption | 0.066 | % |