| Young's modulus | 1850 | MPa |
| Shear modulus | 1150 | MPa |
| Tensile strength | 82.5 | MPa |
| Elongation | 156 | % |
| Compressive strength | 66 | MPa |
| Fatigue | 22 | MPa |
| Bending strength | 120 | MPa |
| Hardness | 115 | Rockwell |
| Impact strength | 0.99 | J/cm |
| Yield strength | 0 | MPa |
| Thermal expansion | 85 | E-6/K |
| Thermal conductivity | 0.2575 | W/m*K |
| Specific heat | 1670 | J/kg*K |
| Vicat | 200 | °C |
| Melting temperature | 257.5 | °C |
| Glass temperature | 78 | °C |
| Minimum service temperature | -60 | °C |
| Maximum service temperature | 160 | °C |
| Density | 1140 | kg/m3 |
| Resistivity | 1E+19 | Ohm*mm2/m |
| Breakdown potential | 16.85 | kV/mm |
| Dielectric loss factor | 0.027 | |
| Friction coefficient | 0.335 | |
| Refraction index | 1.53 | |
| Shrinkage | 1.15 | % |
| Water absorption | 3.25 | % |