| Young's modulus | 2200 | MPa |
| Shear modulus | 800 | MPa |
| Tensile strength | 43.5 | MPa |
| Elongation | 30 | % |
| Compressive strength | 50 | MPa |
| Bending strength | 72.5 | MPa |
| Impact strength | 2.05 | J/cm |
| Yield strength | 0 | MPa |
| Thermal expansion | 95 | E-6/K |
| Thermal conductivity | 0.175 | W/m*K |
| Specific heat | 1300 | J/kg*K |
| Vicat | 98 | °C |
| Minimum service temperature | -40 | °C |
| Maximum service temperature | 75 | °C |
| Density | 1050 | kg/m3 |
| Resistivity | 1E+19 | Ohm*mm2/m |
| Breakdown potential | 38 | kV/mm |
| Dielectric loss factor | 0.035 | |
| Friction coefficient | 0 | |
| Shrinkage | 0.55 | % |